US20080178358A1 - Soft armor - Google Patents
Soft armor Download PDFInfo
- Publication number
- US20080178358A1 US20080178358A1 US11/768,174 US76817407A US2008178358A1 US 20080178358 A1 US20080178358 A1 US 20080178358A1 US 76817407 A US76817407 A US 76817407A US 2008178358 A1 US2008178358 A1 US 2008178358A1
- Authority
- US
- United States
- Prior art keywords
- armor
- layers
- section
- soft
- fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
Soft armor is disclosed. The soft armor comprises an armor structure having a threat side and an inner side inward of the threat side. The armor structure is formed from soft armor material, and the armor structure is substantially imperforable by rifle fire.
Description
- This application is a continuation of U.S. patent application Ser. No. 10/987,310, filed Nov. 12, 2004, which claims the benefit under 35 U.S.C. § 119(e) of U.S. Provisional Patent Application No. 60/520,263, filed Nov. 14, 2003, titled SOFT ARMOR. The entire contents of the above-noted provisional patent application are hereby incorporated by reference herein and made a part of this specification.
- 1. Field of the Invention
- Certain disclosed embodiments relate generally to armor for protection of personnel and/or vehicles, buildings, etc.
- 2. Description of the Related Art
- Currently known armor includes “hard” and “soft” armor. Hard armor can be made very strong, but may be too rigid for some applications. Soft armor has some advantages, but is generally weaker than hard armor.
- According to one embodiment, there is provided soft armor. The soft armor comprises an armor structure having a threat side and an inner side inward of the threat side. The armor structure is formed from soft armor material, and the armor structure is substantially imperforable by rifle fire.
- According to another embodiment, there is provided soft armor. The soft armor comprises an armor structure having a threat side and an inner side inward of the threat side. The armor structure is formed from soft armor material, and the armor structure is sufficiently strong to defeat rifle fire.
- According to another embodiment, there is provided soft armor. The soft armor comprises an armor structure having a threat side and an inner side inward of the threat side. The armor structure is formed from soft armor material, and the armor structure provides at least NIJ type III ballistic protection.
- According to another embodiment, there is provided a soft armor garment. The soft armor garment comprises a torso portion formed from soft armor material and configured to wrap around a torso of a wearer. The torso portion provides at least NIJ type III ballistic protection to at least a portion of the torso against threats from any side of the torso.
- According to another embodiment, there is provided a soft armor garment. The soft armor garment comprises a torso portion formed from soft armor material and configured to wrap around a torso of a wearer. The torso portion provides at least NIJ type III ballistic protection to the torso against threats within a 360-degree threat envelope.
- Certain objects and advantages of the invention are described herein. Of course, it is to be understood that not necessarily all such objects or advantages may be achieved in accordance with any particular embodiment of the invention. Thus, for example, those skilled in the art will recognize that the invention may be embodied or carried out in a manner that achieves or optimizes one advantage or group of advantages as taught herein without necessarily achieving other objects or advantages as may be taught or suggested herein.
- All of the embodiments summarized above are intended to be within the scope of the invention herein disclosed. However, despite the foregoing discussion of certain embodiments, only the appended claims (and not the present summary) are intended to define the invention. The summarized embodiments, and other embodiments of the present invention, will become readily apparent to those skilled in the art from the following detailed description of the preferred embodiments having reference to the attached figures, the invention not being limited to any particular embodiment(s) disclosed.
-
FIG. 1 is a schematic sectional view of one embodiment of an armor structure. -
FIG. 2 is a schematic sectional view of another embodiment of an armor structure. -
FIG. 3 is a schematic sectional view of another embodiment of an armor structure. -
FIG. 4 is a schematic sectional view of another embodiment of an armor structure. -
FIG. 5 is a schematic sectional view of another embodiment of an armor structure. -
FIG. 6 is a schematic sectional view of another embodiment of an armor structure. -
FIG. 7 is a schematic top view of an armored vest and a threat envelope defeated by the armored vest. -
FIG. 8 is a front view of another embodiment of an armored vest. -
FIG. 9 is a rear view of the armored vest ofFIG. 8 . -
FIG. 10 is a front view of another embodiment of an armored vest. -
FIG. 11 is a schematic exploded sectional view of a technique usable for constructing various armor structures disclosed herein. -
FIG. 12 is an elevation view of a stitch pattern usable for constructing various armor structures disclosed herein. -
FIG. 13 is an elevation view of another stitch pattern usable for constructing various armor structures disclosed herein. -
FIG. 1 depicts one embodiment of asoft armor structure 100 which generally comprises a layered construction of afirst section 110,second section 120 andthird section 130. Thearmor structure 100 is configured to be worn, mounted or otherwise employed such that thefirst section 110 is located closest to a threat (e.g., incoming gunfire) and thethird section 130 is located closest to the wearer, vehicle, aircraft, building, etc. to be protected by thearmor structure 100. Accordingly, thearmor structure 100 includes athreat side 140 and aninner side 150. - In some embodiments, each of the first, second and
third sections first section 110 comprises ZYLON® (used herein to refer to PBO (poly(p-phenylene-2,6-benzobisoxazole)) material or fabric formed therefrom), thesecond section 120 comprises KEVLAR® (used herein to refer to para-aramid material or fabric formed therefrom), and thethird section 130 comprises KEVLAR. In still other such embodiments, any one or more of the first, second andthird sections - In one such embodiment, the
first section 110 comprises 10 layers of ZYLON-530 (i.e., ZYLON similar to style no. 530 available from Hexcel Schwebel of Anderson, S.C.), thesecond section 120 comprises 6 layers of KEVLAR-704 (i.e., KEVLAR similar to style no. 704 available from Hexcel Schwebel), and thethird section 130 comprises 8 layers of KEVLAR-726 (i.e., KEVLAR similar to style no. 726 available from Hexcel Schwebel). (In addition, if desired, the layers of thethird section 130 may be laminated to improve resistance to backface deformation.) This embodiment of thearmor structure 100 achieves type IIIa protection as established in the National Institute of Justice (“NIJ”) standard no. 0101.04 (June 2001). In addition, this embodiment of thearmor structure 100 protects against the following “supplemental” threats under test circumstances similar to those set forth in NIJ standard no. 0101.04: (1) a 60 grain, 9 mm RBCD armor-piercing bullet at 2105 feet per second (FPS); (2) a 52 grain, 9 mm MagSafe Agent Load bullet at 2120 FPS; (3) a 77 grain, .40 caliber MagSafe bullet at 1920 FPS; and (4) a 92 grain, .45 caliber MagSafe Agent Load bullet at 2020 FPS. - In further type IIIa-compliant embodiments of the
armor structure 100, thefirst section 110 comprises 10 or more (e.g., 11, 12, 15, 20, 25 or more) layers of ZYLON-530, thesecond section 120 comprises 6 or more (e.g., 7, 8, 10, 12, 15, 20 or more) layers of KEVLAR-704, and thethird section 130 comprises 8 or more (e.g., 9, 10, 12, 15, 20 or more) layers of KEVLAR-726. (In certain of these embodiments, one or more layers of soft armor material other than ZYLON-530, KEVLAR-704 and KEVLAR-726 may be employed in the first, second orthird layers - In still further type IIIa-compliant embodiments of the
armor structure 100, an “overbuilt” section (i.e., more than 10 (e.g., 11, 12, 15, 20, 25 or more) layers of ZYLON-530 employed in thefirst section 110, more than 6 (e.g., 7, 8, 10, 12, 15, 20 or more) layers of KEVLAR-704 employed in thesecond section 120, or more than 8 (e.g., 9, 10, 12, 15, 20 or more) layers of KEVLAR-726 employed in the third section 130) is employed in one or two of thesections first section 110, fewer than 6 layers of KEVLAR-704 employed in thesecond section 120, or fewer than 8 layers or KEVLAR-726) is employed in the balance of thesections armor structure 100, such an “overbuilt” section is employed as one or two of thesections sections -
FIG. 2 depicts another embodiment of asoft armor structure 200 which generally comprises a layered construction of afirst section 210 and asecond section 220. Thearmor structure 200 is configured to be worn, mounted or otherwise employed such that thefirst section 210 is located closest to a threat (e.g., incoming gunfire) and thesecond section 220 is located closest to the wearer, vehicle, aircraft, building, etc. to be protected by thearmor structure 200. Accordingly, thearmor structure 200 includes athreat side 240 and aninner side 250. - In some embodiments, both of the first and
second sections first section 210 comprises ZYLON and thesecond section 220 comprises KEVLAR. In still other such embodiments, one or both of the first andsecond sections - In one such embodiment, the
first section 210 comprises 22 layers of ZYLON-530 and thesecond section 220 comprises 3 layers of KEVLAR-726. (In addition, if desired, the layers of thesecond section 220 may be laminated to improve resistance to backface deformation.) This embodiment of thearmor structure 200 achieves NIJ type IIIa protection. In addition, this embodiment of thearmor structure 200 protects against the following “supplemental” threats under test circumstances similar to those set forth in NIJ standard no. 0101.04: (1) a 60 grain, 9 mm RBCD armor-piercing bullet at 2600 feet per second (FPS); (2) a 52 grain, 9 mm MagSafe Agent Load bullet at 2600 FPS; (3) a 77 grain, .40 caliber MagSafe bullet at 2400 FPS; and (4) a 92 grain, .45 caliber MagSafe Agent Load bullet at 2500 FPS. - In further type lIIa-compliant embodiments of the
armor structure 200, thefirst section 210 comprises 22 or more (e.g., 23, 24, 25, 30, 35, 40, 50 or more) layers of ZYLON-530, and thesecond section 220 comprises 3 or more (e.g., 4, 5, 6, 9, 10, 12, 15 or more) layers of KEVLAR-726. (In these embodiments, one or more layers of soft armor material other than ZYLON-530 or KEVLAR-726 may be employed in the first orsecond layers - In still further type IIIa-compliant embodiments of the
armor structure 200, an “overbuilt” section (i.e., more than 22 (e.g., 23, 24, 25, 30, 35, 40, 50 or more) layers of ZYLON-530 employed in thefirst section 210, or more than 3 (e.g., 4, 5, 6, 9, 10, 12, 15 or more) layers of KEVLAR-726 employed in the second section 220) is employed in one of thesections first section 210, or fewer than 3 layers of KEVLAR-726 employed in the second section 220) is employed in the other of thesections armor structure 200, such an “overbuilt” section is employed as one of thesections sections -
FIG. 3 depicts another embodiment of asoft armor structure 300 which generally comprises a first armor substructure comprising any of the embodiments disclosed herein of thearmor structure 100, positioned adjacent a second armor substructure comprising any of the embodiments disclosed herein of thearmor structure 200. Thearmor structure 300 is configured to be worn, mounted or otherwise employed such that thefirst section 110 of thearmor structure 100 is located closest to a threat (e.g., incoming gunfire) and thesecond section 220 of thearmor structure 200 is located closest to the wearer, vehicle, aircraft, building, etc. to be protected by thearmor structure 300. Accordingly, thearmor structure 300 includes athreat side 340 and aninner side 350. The various embodiments of thearmor structure 300 defeat handgun fire and various “supplemental” threats as discussed above, and achieve NIJ type IIIa protection. -
FIG. 4 depicts another embodiment of asoft armor structure 400 which generally comprises a layered construction of afirst section 410 and asecond section 420. Thearmor structure 400 is configured to be worn, mounted or otherwise employed such that thefirst section 410 is located closest to a threat (e.g., incoming gunfire) and thesecond section 420 is located closest to the wearer, vehicle, aircraft, building, etc. to be protected by thearmor structure 400. Accordingly, thearmor structure 400 includes athreat side 440 and aninner side 450. - In some embodiments, both of the first and
second sections first section 410 comprises ZYLON and thesecond section 420 comprises KEVLAR. In still other such embodiments, one or both of the first andsecond sections - In one such embodiment, the
first section 410 comprises 90 layers of ZYLON-530 and thesecond section 420 comprises 26 layers of KEVLAR-726. (In addition, if desired, the layers of thesecond section 420 may be laminated to improve resistance to backface deformation.) This embodiment of thearmor structure 400 defeats both handgun and rifle fire, and achieves NIJ type III protection. - In further type III-compliant embodiments of the
armor structure 400, thefirst section 410 comprises 90 or more (e.g., 91, 92, 95, 100, 110, 125, 150 or more) layers of ZYLON-530, and thesecond section 220 comprises 26 or more (e.g., 27, 28, 30, 35, 40, 50 or more) layers of KEVLAR-726. (In these embodiments, one or more layers of soft armor material other than ZYLON-530 or KEVLAR-726 may be employed in the first orsecond layers - In still further type III-compliant embodiments of the
armor structure 400, an “overbuilt” section (i.e., more than 90 (e.g., 91, 92, 95, 100, 110, 125, 150 or more) layers of ZYLON-530 employed in thefirst section 410, or more than 26 (e.g., 27, 28, 30, 35, 40, 50 or more) layers of KEVLAR-726 employed in the second section 420) is employed in one of thesections first section 410, or fewer than 26 layers of KEVLAR-726 employed in the second section 420) is employed in the other of thesections armor structure 400, such an “overbuilt” section is employed as one of thesections sections -
FIG. 5 depicts another embodiment of asoft armor structure 500 which generally comprises asingle section 510 formed from soft armor material and having athreat side 540 and aninner side 550. Thearmor structure 500 is configured to be worn, mounted or otherwise employed to protect a human wearer, vehicle, aircraft, building, etc. - In some embodiments, the
armor structure 500 is formed from ZYLON; in certain such embodiments, thearmor structure 500 may be formed from woven ZYLON, or multiple layers of woven ZYLON. In still another such embodiment,armor structure 500 comprises 258 layers of ZYLON-530. This embodiment of thearmor structure 500 defeats both handgun and rifle fire, and achieves NIJ type III protection. - In further type III-compliant embodiments of the
armor structure 500, thestructure 500 comprises 258 or more (e.g., 259, 260, 265, 275, 300, 350, 400 or more) layers of ZYLON-530. (In these embodiments, one or more layers of soft armor material other than ZYLON-530 may be employed in addition to the layers specified above.) -
FIG. 6 depicts another embodiment of asoft armor structure 600 which generally comprises a layered construction of afirst section 610 and asecond section 620. Thearmor structure 600 is configured to be worn, mounted or otherwise employed such that thefirst section 610 is located closest to a threat (e.g., incoming gunfire) and thesecond section 620 is located closest to the wearer, vehicle, aircraft, building, etc. to be protected by thearmor structure 600. Accordingly, thearmor structure 600 includes athreat side 640 and aninner side 650. - In some embodiments, both of the first and
second sections first section 610 comprises ZYLON and thesecond section 620 comprises SPECTRASHIELD PLUS® (used herein to refer to ultra-high molecular weight polyethylene or fabric formed therefrom). In still other such embodiments, one or both of the first andsecond sections - In one such embodiment, the
first section 610 comprises 100 layers of ZYLON-530 and thesecond section 620 comprises 135 layers of SPECTRASHIELD PLUS-902 (i.e., SPECTRASHIELD PLUS similar to style no. 902 available from Hexcel Schwebel of Anderson, S.C., or from Honeywell Corp. of Morristown, N.J.). This embodiment of thearmor structure 600 defeats both handgun and rifle fire, and achieves NIJ type III protection. - In further type III-compliant embodiments of the
armor structure 600, thefirst section 610 comprises 100 or more (e.g., 101, 102, 105, 110, 125, 150, 200 or more) layers of ZYLON-530, and thesecond section 220 comprises 135 or more (e.g., 136, 137, 140, 150, 175, 200 or more) layers of SPECTRASHIELD PLUS-902. (In these embodiments, one or more layers of soft armor material other than ZYLON-530 or SPECTRASHIELD PLUS-902 may be employed in the first orsecond layers - In still further type III-compliant embodiments of the
armor structure 600, an “overbuilt” section (i.e., more than 100 (e.g., 101, 102, 105, 110, 125, 150, 200 or more) layers of ZYLON-530 employed in thefirst section 610, or more than 135 (e.g., 136, 137, 140, 150, 175, 200 or more) layers of SPECTRASHIELD PLUS-902 employed in the second section 620) is employed in one of thesections first section 610, or fewer than 135 layers of KEVLAR-726 employed in the second section 620) is employed in the other of thesections armor structure 600, such an “overbuilt” section is employed as one of thesections sections - Any of the embodiments of the
soft armor structures FIG. 7 , such avest 705 is entirely constructed from one or a combination of the armor structures disclosed herein, providing ballistic protection of a given type (e.g., type IIIa, type III, type 2.7A, rifle-fire-defeating) that “wraps” completely around a torso T of a wearer W. In other words, such a vest provides 360-degree protection for the torso T (at the ballistic protection level provided by thearmor structure 100/200/300/400/500/600 chosen to construct the vest 705), by defeatingthreats 715 approaching the standing/kneeling/sitting wearer W from any angle as depicted inFIG. 7 . (For example, “360-degree” level III protection may be facilitated by constructing thevest 705 from any suitable embodiment of thearmor structures 300/400/500/600 disclosed above.) Thevest 705 may also be configured to cover the tops of the wearer's shoulders, to protect the torso T from threats from above. -
FIGS. 8-9 depict front and rear views, respectively, of another embodiment of avest 805 that may be constructed with any one or combination of thearmor structures 100/200/300/400/500/600 disclosed herein. (The dimensions and specifications listed onFIGS. 8-9 are merely exemplary, and may be varied or omitted in other embodiments of thevest 805.) Thevest 805 generally comprises atorso cover 807 and one ormore trauma plates 809. The torso cover may be constructed from any of the armor structures disclosed herein, or any other suitable material, and the trauma plate(s) 809 may likewise be constructed from any of the herein-disclosed armor structures. Thetorso cover 807 extends behind or in front of the trauma plate(s) 809 so that enhanced protection is provided at the trauma plate(s). As seen inFIG. 9 , the rear of thevest 805 may feature a spinal trauma plate to provide added protection at the wearer's spinal region. The spinal trauma plate may be formed from any of the armor structures disclosed herein, or may be formed from an outer section of 5 or more layers of ZYLON-530, a middle section of 6 or more layers of KEVLAR-726, and an inner section of 4 or more layers of KEVLAR-724 (i.e., KEVLAR similar to style no. 704 available from Hexcel Schwebel). -
FIG. 10 depicts a front view of another embodiment of thevest 805, which may be generally similar to the embodiment of thevest 805 shown inFIGS. 8-9 , except as indicated inFIG. 10 . (As withFIGS. 8-9 , the dimensions and specifications listed onFIG. 10 are merely exemplary, and may be varied or omitted in other embodiments of thevest 805.) - Alternatively, any of the disclosed armor structures may be employed to construct soft body armor panels which may be sewn into, and/or enclosed in pockets formed in, a vest constructed from other suitable materials or fabrics.
- Any of the disclosed
armor structures armor structures - In constructing the armor structures and/or armored articles disclosed herein, each of the layers of soft armor material may be laser-cut into the desired perimeter shape. The layers may be cut individually or in groups of 2 or more. Laser cutting has proven advantageous in that it prevents fraying of woven soft armor materials as the laser heat tends to “heat-seal” the edges of the cut material. In some embodiments, an infrared laser or a carbon-dioxide laser may be employed.
-
FIG. 11 depicts a construction technique that may be employed in joining together a number (e.g., 5, 10 or more) oflayers 902 of soft armor material, to form a section or partial section of any of thearmor structures 100/200/300/400/500/600 disclosed herein, or to form a complete armor structure. The technique involves applying anadhesive tape 904, such as a polymer tape, over some or all of the perimeter edges of the “sandwich” oflayers 902. (In one embodiment, a polyethylene tape is employed.) After thetape 904 is applied, stitching 906 is passed through thetape 904 andlayers 902, using any suitable stitching process. The technique illustrated inFIG. 11 may be employed in addition to the laser-cutting technique disclosed above. -
FIG. 12 depicts a stitch pattern that may be employed in stitching together a number of sections, layers, etc. to form any of the armor structures disclosed herein, or to form an armor panel or other armored article. The pattern includes a number (8 are depicted; alternatively, a smaller or larger number may be employed) ofradial stitch lines 1002 that pass through the approximate center C of a panel/article 1000. In one embodiment, as shown inFIG. 12 , theradial stitch lines 1002 are approximately equally angularly spaced about the center C. A number of optionalperimeter stitch lines 1004 may also be employed near the edges of the panel/article 1000. (Although a square panel/article 1000 is depicted inFIG. 12 , the depicted stitch pattern may be used in constructing panels/articles having any of a variety of perimeter shapes.) -
FIG. 13 depicts another stitch pattern that may be employed in stitching together a number of sections, layers, etc. to form any of the armor structures disclosed herein, or to form an armor panel or other armored article. Like the pattern shown inFIG. 12 , the “spider-web” pattern ofFIG. 13 includes a number ofradial stitch lines 1002 that pass through the approximate center C of the panel/article 1000. A number of generally concentriccircular stitch lines 1006 are also made to create the spider-web form shown inFIG. 13 . - Either of the stitch patterns shown in
FIG. 12 or 13, or any other suitable stitch pattern, may be employed with the laser cutting procedure disclosed above, and/or the construction technique shown inFIG. 11 , in constructing any of the armor structures or armored articles disclosed herein. In addition, any of the armor structures, panels, sections etc. may be encased in an appropriate structural or waterproofing casing during or after fabrication. - Specifications for various materials discussed above are as set forth in the following tables.
-
ZYLON-530: SPECIFICATIONS Yarn Type Warp Yarn Zylon AS, 500 denier Fill Yarn Zylon AS, 500 denier Fabric Weight 4.00 oz/yd2 136 g/m2 Weave Style Plain Nominal Construction Warp Count 30 (yarns/inch) Fill Count 30 Fabric Thickness 8.0 mils 0.20 mm Breaking Strength 1080 lbf/in 1020 lbf/in -
KEVLAR-704: SPECIFICATIONS Yarn Type Warp Yarn Keviar 129, 840 denier Fill Yarn Keviar 129, 840 denier Fabric Weight 7.0 oz/yd2 237 g/m2 Weave Style Plain Nominal Construction Warp Count 31 (yarns/inch) Fill Count 31 Fabric Thickness 12.0 mils 0.3 mm Breaking Strength 900 lbf/in 950 lbf/in -
KEVLAR-724: SPECIFICATIONS Yarn Type Warp Yarn Kevlar 129, 1000 denier Fill Yarn Kevlar 129, 1000 denier Fabric Weight 6.5 oz/yd2 220 g/m2 Weave Style Plain Nominal Construction Warp Count 24 (yarns/inch) Fill Count 24 Fabric Thickness 11.0 mils 0.28 mm Breaking Strength 763 lbf/in 776 lbf/in -
KEVLAR-726: SPECIFICATIONS Yarn Type Warp Yarn Kevlar 129, 840 denier Fill Yarn Kevlar 129, 840 denier Fabric Weight 6.0 oz/yd2 203 g/m2 Weave Style Plain Nominal Construction Warp Count 26 (yarns/inch) Fill Count 26 Fabric Thickness 10.0 mils 0.25 mm Breaking Strength 760 lbf/in 770 lbf/in -
SPECTRASHIELD PLUS-902: SPECIFICATIONS Yarn Type Warp Yarn Spectra 900, 1200 denier Fill Yarn Spectra 900, 1200 denier Fabric Weight 5.5 oz/yd2 187 g/m2 Weave Style Plain Nominal Construction Warp Count 17 (yarns/inch) Fill Count 17 Fabric Thickness 18.0 mils 0.46 mm Breaking Strength 900 lbf/in 850 lbf/in - Although this invention has been disclosed in the context of certain preferred embodiments and examples, it will be understood by those skilled in the art that the present invention extends beyond the specifically disclosed embodiments to other alternative embodiments and/or uses of the invention and obvious modifications and equivalents thereof. Thus, it is intended that the scope of the present invention herein disclosed should not be limited by the particular disclosed embodiments described above, but should be determined only by a fair reading of the claims that follow.
Claims (20)
1. Soft armor comprising:
an armor structure having a threat side and an inner side inward of said threat side;
said armor structure being formed from soft armor material;
said armor structure being substantially imperforable by rifle fire.
2. The soft armor of claim 1 , wherein the soft armor material comprises a number of ballistic material layers, said ballistic material layers having a combined nominal thickness of 25.8 mm-82.1 mm.
3. The soft armor of claim 1 , wherein the soft armor material comprises a number of ballistic material layers, said ballistic material layers have a combined nominal weight of 542-1142.5 ounces per square yard.
4. The soft armor of claim 1 , wherein said armor structure comprises at least 258 layers of PBO fabric.
5. The soft armor of claim 1 , wherein said armor structure comprises a first section of at least 100 layers of PBO fabric, adjacent to a second section of at least 135 layers of ultra-high molecular weight polyethylene fabric.
6. The soft armor of claim 1 , wherein said armor structure comprises a first section of at least 90 layers of PBO fabric, adjacent to a second section of at least 26 layers of para-aramid fabric.
7. An armor panel formed from the soft armor of claim 1 .
8. A garment comprising at least one of the armor panel of claim 7 .
9. A vest comprising at least one of the armor panel of claim 7 .
10. A helmet comprising the soft armor of claim 1 .
11. Soft armor comprising:
an armor structure having a threat side and an inner side inward of said threat side;
said armor structure being formed from soft armor material;
said armor structure providing at least NIJ type III ballistic protection.
12. The soft armor of claim 11 , wherein the soft armor material comprises a number of fabric layers, said fabric layers having a combined nominal thickness of 25.8 mm-82.1 mm and a combined nominal weight of 542-1142.5 ounces per square yard.
13. The soft armor of claim 11 , wherein said armor structure comprises at least 258 layers of PBO fabric.
14. The soft armor of claim 11 , wherein said armor structure comprises a first section of at least 100 layers of PBO fabric, adjacent to a second section of at least 135 layers of ultra-high molecular weight polyethylene fabric.
15. The soft armor of claim 11 , wherein said armor structure comprises a first section of at least 90 layers of PBO fabric, adjacent to a second section of at least 26 layers of para-aramid fabric.
16. An armor panel formed from the soft armor of claim 11 .
17. A garment comprising at least one of the armor panel of claim 16 .
18. The garment of claim 17 , comprising a torso portion formed from the soft armor material and configured to wrap around a torso of a wearer, said torso portion providing at least NIJ type III ballistic protection against threats within a 360-degree threat envelope.
19. A helmet comprising the soft armor of claim 11 .
20. Soft armor comprising:
an armor structure having a threat side and an inner side inward of said threat side;
said armor structure being formed from soft armor material;
said armor structure being substantially imperforable by armor-piercing handgun fire;
wherein said armor structure comprises:
a first section of at least 10 layers of PBO fabric, overlying a second section of at least 6 layers of para-aramid fabric, overlying a third section of at least 8 layers of para-aramid fabric.